BRC-843M: Difunctional Aliphatic Hydrophobic Urethane Acrylate

BRC-843M is a difunctional, hydrophobic urethane acrylate which can be formulated to be used in heavy-duty industrial and commercial applications. The resulting tough film makes an effective, non-yellowing, protective single coating that extends the substrates use-life. The low water absorption and alkaline resistance make this oligomer perfect for the following industries: aerospace, appliance, automotive, cosmetic, electronic, industrial, medicaldevice, metal finishing, and UV-curable inks & coatings. BRC-843M exhibits retention of mechanical properties after exposure to high temperatures (200°C for 30 minutes). In addition to the adhesion properties listed in the table below, BRC-843M also shows excellent adhesion to ABS, PVC, PMMA, and polystyrene.

Neat Properties
Property Value
Viscosity cP (60ºC) 21,000
Pt-Co (APHA) Color 42
Refractive Index (25ºC) 1.48
Density, g/cm3 (25ºC) 1.12
Monomer Dilution Properties
Value
Property I30 I50 TM50 TP50 H50 HE30
Tensile Strength (MPa [psi]) 12.4 [1800] 26.9 [3900] 31.7 [4600] 15.9 [2300] 26.9 [3900] 20.7 [3000]
Elongation (%) 80 120 3.7 11 8.6 100
Elastic Modulus (MPa [ksi]) 124.1 [18] 586.1 [85] 1,172.1 [170] 413.7 [60] 620.5 [90] 344.7 [50]
Durometer Hardness 50D 67D 84D 70D 74D 63D
Water Absorption (%) 24hrs 0.41 0.26 0.48 0.56 0.4 1.8
MEK Double Rubs (#) 57 8 >200 67 50 25
Viscosity (cP) 16,000 @ 25ºC 2,000 @ 25ºC 10,000 @ 25ºC 2,000 @ 25ºC 1,000 @ 25ºC 5,800 @ 25ºC

** Tensile Properties per ASTM D882   - Not Tested   || Incompatible   X Unable to Measure

Features

  • Improves adhesion
  • Enhances hardness
  • High temperature resistance
  • Increases weatherability
  • Provides abrasion resistance
  • Low water absorption

Applications

  • Nail gels
  • Industrial coatings
  • 3D printing